PolyOne Geon™ HTX M6215 Polyvinyl Chloride Alloy (PVC Alloy)

Category Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer PolyOne Corporation
Trade Name Geon™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Geon™ HTX M6215 Polyvinyl Chloride Alloy (PVC Alloy).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
It is recommended that the compound pellets be dried for 3 to 4 hours at 150 deg. F.Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.26 g/cc
1.26 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0020 - 0.0050 cm/cm
0.0020 - 0.0050 in/in
ASTM D955
Spiral Flow 86.4 cm
34.0 in
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
ASTM D2240
Tensile Strength, Yield 44.1 MPa
6400 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 73.8 MPa
10700 psi
ASTM D790
Flexural Modulus 2.39 GPa
347 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.18 mm,
Temperature 0.000 °C
3.00 ft-lb/in

@Thickness 0.125 in,
Temperature 32.0 °F
Injection Molded; ASTM D256A
2.70 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
5.06 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 77.8 °C

@Thickness 6.35 mm
172 °F

@Thickness 0.250 in
Unannealed; ASTM D648
87.2 °C

@Thickness 6.35 mm
189 °F

@Thickness 0.250 in
Annealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 72.8 °C

@Thickness 6.35 mm
163 °F

@Thickness 0.250 in
Unannealed; ASTM D648
85.0 °C

@Thickness 6.35 mm
185 °F

@Thickness 0.250 in
Annealed; ASTM D648
UL RTI, Electrical 50.0 °C
122 °F
UL 746
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746
Flammability, UL94 V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
All Colors
V-0

@Thickness 1.60 mm
V-0

@Thickness 0.0630 in
ALL; UL 94
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
ALL; UL 94
5VA

@Thickness 1.60 mm
5VA

@Thickness 0.0630 in
All Colors
Processing Properties Metric English Comments
Melt Temperature 202 - 210 °C
396 - 410 °F
Descriptive Properties Value Comments
Automotive Specifications CHRYSLER MS-DC28 Type B
GM GMP.PVC.034
Features General Purpose
High Flow
Medium Impact Resistance
Forms Pellets
Generic Material PVC Alloy
Generic Name Polyvinyl Chloride Alloy (PVC Alloy)
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Appliances