PolyOne Geon™ Specialty Suspension Impel S100 Polyvinyl Chloride Homopolymer (PVC Homopolymer)

Category	Polymer , Thermoplastic , Vinyl (PVC)
Manufacturer	PolyOne Corporation
Trade Name	Geon™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Geon™ Specialty Suspension Impel S100 Polyvinyl Chloride Homopolymer (PVC Homopolymer).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Geon® Impel S100 is a homopolymer specialty suspension resin intended for use in highly plasticized extrusion and injection molding formulations. It gives superior plasticizer absorption properties allowing the production of low durometer compounds. Quick plasticizer uptake provides a reduction of mix time allowing the higher production rate, reducing compounding times and manufacturing costs.Note: The value set forth represent 'typical' values and PolyOne Corporation, therefore, makes no representation that the material in any particular shipment will conform to the listed properties. Packaging: This resin is shipped in multi-wall paper bags, netweight 50lbs, 2,500lbs per pallet. Information shown on the package includes commercial identification number, lot, and weight. STP 488 (formulation): 100phr Geon® Impel S100, 55phr TOTM, and 18phr FillerInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.40 g/cc	1.40 g/cc	ASTM D792
Volatiles	0.070 %	0.070 %	Geon® STP 793; Internal Method
Apparent Bulk Density	0.410 g/cc	0.0148 lb/in³	Geon® STP 1169; Internal Method
Porosity	0.53 %	0.53 %	cm³/g; Geon® STP 1094; Internal Method
Particle Size	<= 105 µm	<= 105 µm	14%; Geon® DFT 1466; Internal Method
	150 µm	150 µm	Average Particle SizeGeon® STP 1466; Internal Method
	>= 250 µm	>= 250 µm	4%; Geon® DFT 1466; Internal Method
Relative Viscosity	2.37 cP	2.37 cP	Correlation, Cyclohexanone 1%; Internal Method
Viscosity Measurement	1.0	1.0	Inherent; ASTM D1243-60-A

Descriptive Properties	Value	Comments
Contamination	0	Internal Method; Magnetic ParticlesGeon® STP 1217 Unit: #/100in2
	18	Internal Method; Dark ParticlesGeon® STP 1217 Unit: #/100in2
	22	Internal Method; Light Colored ParticlesGeon® STP 1217 Unit: #/100in2
Flow Time	34 sec	Internal Method; Conditioned Funnel Flow TimeGeon® STP 1169
Forms	Powder	White powder
Generic Material	PVC Homopolymer
Generic Name	Polyvinyl Chloride Homopolymer (PVC Homopolymer)
K-Value	70	Internal Method; Correlation, 0.5g/ 100ml
Polymerization Process	Suspension
Powder Mix Time	4.4 min	Internal Method; Geon® STP 488 (with provided formula)
Processing Method	Calendering
	Extrusion
	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Residual Vinyl Chloride Monomer	< 1 ppm	Internal Method; Geon® STP 1005
Uses	Insulation
	Wire & Cable Applications