PolyOne LubriOne™ PC-000/15T Polycarbonate (PC)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer PolyOne Corporation
Trade Name LubriOne™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne LubriOne™ PC-000/15T Polycarbonate (PC).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.28 g/cc
1.28 g/cc
ASTM D792
Water Absorption 0.18 %

@Thickness 0.508 mm
0.18 %

@Thickness 0.0200 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 55.2 MPa
8010 psi
Type I, 5.1 mm/min; ASTM D638
Elongation at Break 8.0 %
8.0 %
Type I, 5.1 mm/min; ASTM D638
Tensile Modulus 2.41 GPa
350 ksi
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.41 GPa
350 ksi
ASTM D790
Izod Impact, Notched 1.30 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
2.44 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Processing Properties Metric English Comments
Melt Temperature 288 - 316 °C
550 - 601 °F
Mold Temperature 121 °C
250 °F
Drying Temperature 121 °C
250 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Features Lubricated
Forms Pellets
Generic Material PC
Generic Name Polycarbonate (PC)
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Uses Appliance Components
Conveyor Parts
Printer Parts
Copyright © lookpolymers.com All Rights Reserved