- PolyOne Nymax™ 1200 IL Natural Polyamide 66 (Nylon 66)
PolyOne Nymax™ 1200 IL Natural Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ 1200 IL Natural Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
The Nymax® 1200 IL is an internally lubricated, unfilled nylon 6/6 designed for exceptional processing and mold release. This grade is intended primarily for injection molded applications where a good balance of strength, toughness, high temperature resistance and surface appearance are required.Molded Test Bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.4 % @Thickness 3.18 mm |
1.4 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.021 cm/cm @Thickness 3.18 mm |
0.021 in/in @Thickness 0.125 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.036 cm/cm @Thickness 3.18 mm |
0.036 in/in @Thickness 0.125 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.8 MPa | 11000 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Strength, Yield | 77.0 MPa | 11200 psi | ISO 527-2 |
| Flexural Strength | 113 MPa | 16400 psi | ASTM D790 |
| 120 MPa | 17400 psi | ISO 178 | |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| 2.90 GPa | 421 ksi | ISO 178 | |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded, Across Flow; ASTM D256A |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO 180/3A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 255 - 265 °C | 491 - 509 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C | 180 °F | Unannealed; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 - 270 °C | 482 - 518 °F | |
| Middle Barrel Temperature | 260 - 280 °C | 500 - 536 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Nozzle Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 60.0 - 107 °C | 140 - 225 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Lubricant | |
| Appearance | Natural Color | |
| Features | General Purpose | |
| Lubricated | ||
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Processing Method | Injection Molding | |
| Regional Availability | North America | |
| South America | ||
| Uses | Automotive Applications | |
| Construction Applications | ||
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications |