PolyOne Nymax™ GF 1200 A 55 HS Black 13 Polyamide 66 (Nylon 66)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer PolyOne Corporation
Trade Name Nymax™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Nymax™ GF 1200 A 55 HS Black 13 Polyamide 66 (Nylon 66).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durability in harsh environments. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipmentMolded Test Bars: Dry as MoldedInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Water Absorption 0.60 %

@Thickness 3.18 mm
0.60 %

@Thickness 0.125 in
@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 193 MPa
28000 psi
Type I, 5.1 mm/min; ASTM D638
Tensile Strength 215 MPa
31200 psi
5.0 mm/min; ISO 527
Elongation at Break 2.5 %
2.5 %
Type I, 5.1 mm/min; ASTM D638
Flexural Strength 310 MPa
45000 psi
ASTM D790
Flexural Modulus 15.2 GPa
2200 ksi
ASTM D790
15.5 GPa
2250 ksi
25 mm/min; ISO 178
Izod Impact, Notched 1.40 J/cm

@Thickness 3.18 mm,
Temperature 23.0 °C
2.62 ft-lb/in

@Thickness 0.125 in,
Temperature 73.4 °F
Injection Molded; ASTM D256A
Izod Impact, Notched (ISO) 12.0 kJ/m²
5.71 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
ASTM D789
Deflection Temperature at 0.46 MPa (66 psi) 257 °C

@Thickness 3.18 mm
495 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 248 °C
478 °F
Unannealed; ISO 75-2
255 °C

@Thickness 3.18 mm
491 °F

@Thickness 0.125 in
Unannealed; ASTM D648
Processing Properties Metric English Comments
Mold Temperature 60.0 - 107 °C
140 - 225 °F
Drying Temperature 82.2 °C
180 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Additive Heat Stabilizer
Appearance Black
Features Heat Stabilized
Filler / Reinforcement Glass Fiber Reinforcement
Unspecified FillerReinfor., 55% Filler by Weight
Forms Pellets
Generic Material Nylon 66
Generic Name Polyamide 66 (Nylon 66)
Regional Availability North America
South America