PolyOne OnFlex™ U 5370A-E0077 Thermoplastic Elastomer (TPE)
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | PolyOne Corporation |
| Trade Name | OnFlex™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne OnFlex™ U 5370A-E0077 Thermoplastic Elastomer (TPE).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
OnFlex™ U thermoplastic elastomer compounds are based on thermoplastic polyurethane elastomers (TPE-U). The OnFlex™ U 5300 series are based upon alloys of SEBS and TPU, combining the advantages of both raw materials, for example the good processability and soft haptic of a TPE-S with the excellent mechanical properties and abrasion resistance of a TPE-U. OnFlex™ U 5300 compounds are formulated to deliver very good scratch resistance, a wide hardness range and good chemical resistance.Properties are measured using injection molded plaques.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | ISO 868 |
| Tensile Strength at Break | 17.7 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2570 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type 2, 200 mm/min Across Flow; ISO 37 |
| 17.7 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2570 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type 2, 200 mm/min; Flow; ISO 37 | |
| Elongation at Break | 570 % @Thickness 2.00 mm, Temperature 23.0 °C |
570 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type 2, 200 mm/min Across Flow; ISO 37 |
| 580 % @Thickness 2.00 mm, Temperature 23.0 °C |
580 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type 2, 200 mm/min; Flow; ISO 37 | |
| Tear Strength | 47.0 kN/m @Thickness 2.00 mm, Temperature 23.0 °C |
268 pli @Thickness 0.0787 in, Temperature 73.4 °F |
Method A, Trouser, 500 mm/min Across Flow; ISO 34-1 |
| 53.0 kN/m @Thickness 2.00 mm, Temperature 23.0 °C |
302 pli @Thickness 0.0787 in, Temperature 73.4 °F |
Method A, Trouser, 500 mm/min; Flow; ISO 34-1 | |
| Abrasion | 35 | 35 | [mm³]; DIN 53516 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 6.0 % | 6.0 % | 60°; ISO 2813 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 170 - 210 °C | 338 - 410 °F | |
| Mold Temperature | 30.0 - 60.0 °C | 86.0 - 140 °F | |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Matte Finish | |
| Features | Good Abrasion Resistance | |
| Oil Resistant | ||
| Scratch Resistant | ||
| Fogging | 1.1 mg | DIN 75201B; 100°C |
| Forms | Pellets | |
| Generic Material | TPE | |
| Generic Material Type | Thermoplastic Polyurethane Elastomer (TPU) | |
| Generic Name | Thermoplastic Elastomer (TPE) | |
| Injection Rate | Slow | |
| Manufacturer / Supplier | GLS Thermoplastic Elastomers | |
| Odor rating | 2.1 | VDA 270 |
| Processing Method | Calendering | |
| Film Extrusion | ||
| Injection Molding | ||
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| RoHS Compliance | RoHS Compliant | |
| Uses | Automotive Applications | |
| Consumer Applications | ||
| General Purpose | ||
| Industrial Applications | ||
| Power/Other Tools |