PolyOne OnForce™ LFT NN-30 LGF/000 Natural Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	OnForce™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne OnForce™ LFT NN-30 LGF/000 Natural Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.37 g/cc	1.37 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0020 - 0.0030 cm/cm	0.0020 - 0.0030 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	183 MPa	26500 psi	ASTM D638
Elongation at Break	2.0 - 3.0 %	2.0 - 3.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	10.3 GPa	1490 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Yield Strength	283 MPa	41000 psi	ASTM D790
Flexural Modulus	9.65 GPa	1400 ksi	ASTM D790
Izod Impact, Notched	2.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	5.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256
Izod Impact, Unnotched	14.0 J/cm	26.2 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	249 °C	480 °F	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	293 - 310 °C	559 - 590 °F
Mold Temperature	93.3 °C	200 °F
Drying Temperature	80.0 °C	176 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Features	Heat Stabilized
Filler / Reinforcement	Long Glass Fiber, 30% Filler by Weight
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
RoHS Compliance	RoHS Compliant