PolyOne Syncure™ System S112BL Polyethylene, Crosslinked (XLPE)

Category	Polymer , Thermoplastic , Polyethylene (PE)
Manufacturer	PolyOne Corporation
Trade Name	Syncure™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Syncure™ System S112BL Polyethylene, Crosslinked (XLPE).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Syncure™ systems are two part moisture crosslinkable compounds. S112BL is a CSA listed, high strength, weather resistant, black (2.5% carbon black) cable insulation compound. RoHS compliant.STORAGE AND HANDLING: Use within 48 hours once package is open to avoid self-curing and scrap.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	0.933 g/cc	0.933 g/cc	ASTM D792
Deformation	7.5 % @Temperature 131 °C, Time 3600 sec	7.5 % @Temperature 268 °F, Time 1.00 hour	500 g; UL 1581

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	48	48	10 sec; ASTM D2240
	52	52	ASTM D2240
Tensile Strength, Yield	15.9 MPa	2310 psi	Type IV, 510 mm/min; ASTM D638
Elongation at Break	500 %	500 %	Type IV, 510 mm/min; ASTM D638
Tear Strength	82.3 kN/m	470 pli	Die C, 2 in/min; ASTM D1004

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.45	2.45	ASTM D150
Dielectric Strength	39.0 kV/mm	991 kV/in	ASTM D149
Dissipation Factor	0.0020	0.0020	ASTM D150

Descriptive Properties	Value	Comments
Agency Ratings	CSA C-22.2 0.3
Appearance	Black
Catalyst Masterbatch	10%	S-1044B
Features	Good Weather Resistance
Forms	Pellets
Gel Content	72%	ASTM D2765; Crosslinked PE, Method B (NonReferee Test)
Generic Material	XLPE
Generic Name	Polyethylene, Crosslinked (XLPE)
Grafted Base Resin	90%	S-1054A
Processing Method	Extrusion Coating
Regional Availability	North America
Retention of Tensile Elongation	90%	121°C, 1.91 mm; 336 hr, UL Standard
Retention of Tensile Strength	95%	121°C, 1.91 mm; 336 hr, UL Standard
Uses	Outdoor Applications
	Wire & Cable Applications
Wire Types	RW-90
	RWU-90