- PolyOne Therma-Tech™ PI-5000 TC Polyetherimide (PEI) (discontinued **)
PolyOne Therma-Tech™ PI-5000 TC Polyetherimide (PEI) (discontinued **)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Therma-Tech™ PI-5000 TC Polyetherimide (PEI)
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Thermally ConductiveElectrically ConductiveUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 131.1 MPa | 19020 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 0.752 % | 0.752 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 31.48 GPa | 4566 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 195.3 MPa | 28330 psi | ASTM D790 |
| Flexural Modulus | 23.4 GPa | 3400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.358 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.670 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 10.8 µm/m-°C @Temperature 20.0 °C |
6.00 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 11.0 W/m-K | >= 76.3 BTU-in/hr-ft²-°F | ASTM C177 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 371 - 399 °C | 700 - 750 °F | Molding |
| Mold Temperature | 135 - 163 °C | 275 - 325 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 6 hour | 6 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- MV Labs PR810 Pr6O11 Praseodymium(III),IV) oxide
- PolyOne Therma-Tech™ SFC-5000 TC Polyphenylene Sulfide (PPS) (discontinued **)
- Kazanorgsintez Pyrolysis Heavy Resin
- Ineos H20A-00 Polypropylene Homopolymer
- Samyang Trirex® 3015NF Polycarbonate, Flame Retardancy
- Zircar Refractory Composites RS-DM Refractory Sheet
- A. Schulman LP544-01 High-Density Copolymer Polyethylene
- Eurotec® Tecopet® PT70 GR30 NL100 HT PET, 30% glass fiber reinforced, high heat stabilized, natural
- Arlon 915-10R##-P1 0.015" (0.381 mm) Cured Self-fusing Silicone Tape
Copyright © lookpolymers.com All Rights Reserved