PolyOne Versollan™ RU 2205-1 Thermoplastic Elastomer (TPE)

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer PolyOne Corporation
Trade Name Versollan™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PolyOne Versollan™ RU 2205-1 Thermoplastic Elastomer (TPE).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Versollan™ RU 2205-1 is the first of a new class of high performance, injection moldable TPU alloys developed to offer a rubbery feel and appearance, reduced cycle times, combined with the performance properties associated with TPUs. - Bonds to PC, ABS, PC/ABS, and Copolyester - Excellent Abrasion Resistance - Fast Set Up Rates During Processing - Matte Finish - Rubbery, Soft Touch Feel - Very Good Oil ResistanceColor concentrates with EVA or LDPE carrier are most suitable for coloring Versollan™ RU 2205-1. Typical letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP). Regrind levels up to 20% can be used with Versollan™ RU 2205-1 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer. Versollan™ RU 2205-1 should not be left in the barrel for extended idle periods (greater than 5 minutes). Suggested Dewpoint: -40°F Injection Speed: 0.5 to 2 in/sec 1st Stage - Boost Pressure: 300 to 700 psi 2nd Stage - Hold Pressure: 30% of Boost Hold Time (Thick Part): 4 to 10 sec Hold Time (Thin Part): 1 to 3 secInformation provided by PolyOne
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Viscosity 14100 cP

@Shear Rate 11200 1/s,
Temperature 200 °C
14100 cP

@Shear Rate 11200 1/s,
Temperature 392 °F
ASTM D3835
Maximum Moisture Content 0.020 - 0.030
0.020 - 0.030
Linear Mold Shrinkage, Flow 0.010 - 0.015 cm/cm
0.010 - 0.015 in/in
ASTM D955
Melt Flow 7.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
7.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
67 g/10 min

@Load 5.00 kg,
Temperature 200 °C
67 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 65
65
10 sec; ASTM D2240
Tensile Strength at Break 13.8 MPa

@Temperature 23.0 °C
2000 psi

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tensile Stress 2.62 MPa

@Strain 100 %,
Temperature 23.0 °C
380 psi

@Strain 100 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
4.21 MPa

@Strain 300 %,
Temperature 23.0 °C
611 psi

@Strain 300 %,
Temperature 73.4 °F
Die C2 hr; ASTM D412
Elongation at Break 710 %

@Temperature 23.0 °C
710 %

@Temperature 73.4 °F
Die C2 hr; ASTM D412
Tear Strength 47.3 kN/m
270 pli
ASTM D624
Compression Set 34 %

@Temperature 23.0 °C,
Time 79200 sec
34 %

@Temperature 73.4 °F,
Time 22.0 hour
ASTM D395B
Thermal Properties Metric English Comments
Brittleness Temperature -67.0 °C
-88.6 °F
Thickness = 1.91mm Conditioned for 40hrs at 23C at 50% RH; ASTM D746
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
1.5mm for US and China; 3.0mm for Canada.; UL 94
Processing Properties Metric English Comments
Rear Barrel Temperature 168 - 188 °C
334 - 370 °F
Middle Barrel Temperature 179 - 199 °C
354 - 390 °F
Front Barrel Temperature 191 - 210 °C
376 - 410 °F
Nozzle Temperature 191 - 216 °C
376 - 421 °F
Melt Temperature 188 - 210 °C
370 - 410 °F
Mold Temperature 21.1 - 32.2 °C
70.0 - 90.0 °F
Drying Temperature 51.7 - 54.4 °C
125 - 130 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Back Pressure 0.000 - 0.862 MPa
0.000 - 125 psi
Screw Speed 75 - 125 rpm
75 - 125 rpm
Descriptive Properties Value Comments
Agency Ratings UL 94 .QMFZ2.E76261
Appearance Natural Color
Features Good Abrasion Resistance
Oil Resistant
Forms Pellets
Generic Material TPE
Generic Name Thermoplastic Elastomer (TPE)
Manufacturer / Supplier GLS Thermoplastic Elastomers
Processing Method Extrusion
Injection Molding
Regional Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
RoHS Compliance RoHS Compliant
Suggested Max Regrind 20%
Uses Consumer Applications
Furniture
Overmolding
Power/Other Tools
Soft Touch Applications