Polycasa SAN
| Category | Polymer , Thermoplastic , SAN Polymer |
| Manufacturer | Polycasa |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polycasa SAN.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
QUINN SAN sheets are characterized by good optical properties and a brilliant surface. The QUINN SAN range contains sheets that are easy to handle, to vacuum form, and show a very good dimensional stability. Typical for QUINN SAN sheets are their very good chemical resistance: they are resistant to most fats, dilute acid solutions, oils and common bleaching agents, as well as some solvents and weak alkaline solutions. The sheets can be used in- and outdoor (in UVP-version) and are resistant to temperature fluctuations. QUINN SAN products can be used in contact with foodstuffs. QUINN SAN material also combines the following excellent properties: High softening point, low water absorption, and high stiffness.Industrial (door) glazing Covers for foodstuffs Covers for office equipment Screen printing Advertising signs Fittings for shops and exhibitions Displays Flat or curved shower screens Greenhouse glazing Room dividersQuinn Manufacturing Group rebranded its Plastics Division as Polycasa in 2013.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 83 | 83 | ISO 2039-2 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-2 |
| Tensile Modulus | 3.90 GPa | 566 ksi | ISO 527-2 |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| Flexural Modulus | 3.75 GPa | 544 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 1.30 kJ/m² | 0.619 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 1.30 J/cm² | 6.19 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 50.0 - 70.0 µm/m-°C @Temperature 20.0 °C |
27.8 - 38.9 µin/in-°F @Temperature 68.0 °F |
DIN 53752 |
| Specific Heat Capacity | 1.38 J/g-°C | 0.330 BTU/lb-°F | ASTM D2766 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 85.0 °C | 185 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 101 °C | 214 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C | 208 °F | ISO 75 |
| Vicat Softening Point | 106 °C | 223 °F | ISO 306 |
| Decomposition Temperature | >= 280 °C | >= 536 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.57 | 1.57 | ISO 489 |
| Transmission, Visible | 86 % | 86 % | DIN 5036-3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 6093 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | IEC 6093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 165 - 190 °C | 329 - 374 °F | Sheet Forming |