Polykemi AB POLYelast TPE Z500 Thermoplastic Elastomer, SEBS-based

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Polykemi AB
Trade Name POLYelast
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYelast TPE Z500 Thermoplastic Elastomer, SEBS-based.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 0.900 g/cc
0.0325 lb/in³
ISO 1183
Linear Mold Shrinkage 0.017 - 0.024 cm/cm
0.017 - 0.024 in/in
With Flow; ISO 2577
0.017 - 0.024 cm/cm
0.017 - 0.024 in/in
Across Flow; ISO 2577
Melt Index of Compound 7.0 g/10 min

@Load 5.00 kg,
Temperature 190 °C
 7.0 g/10 min

@Load 11.0 lb,
Temperature 374 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 50

@Time 15.0 sec
 50

@Time 0.00417 hour
 Polykemi
Tensile Strength at Break <= 6.50 MPa
<= 943 psi
ISO/R527
Elongation at Break 750 %
750 %
ISO/R527
100% Modulus 0.00180 GPa
0.261 ksi
ISO/R527
300% Modulus 0.00260 GPa
0.377 ksi
ISO/R527
Tear Strength 19.0 kN/m
108 pli
D624
Compression Set 20 %

@Temperature 23.0 °C,
Time 259000 sec
 20 %

@Temperature 73.4 °F,
Time 72.0 hour
 DIN 53517
38 %

@Temperature 70.0 °C,
Time 86400 sec
 38 %

@Temperature 158 °F,
Time 24.0 hour
 DIN 53517
Processing Properties Metric English Comments
Melt Temperature 180 - 220 °C
356 - 428 °F
Mold Temperature 20.0 - 40.0 °C
68.0 - 104 °F
Back Pressure 0.500 - 1.50 MPa
72.5 - 218 psi
Descriptive Properties Value Comments
Holding Pressure () Low
% of injection pressure
Injection Pressure Low
Injection Speed () High