Polykemi AB POLYlux 3709MLB PC/PBT-Blend, Paintable

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer Polykemi AB
Trade Name POLYlux
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB POLYlux 3709MLB PC/PBT-Blend, Paintable.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Linear Mold Shrinkage 0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
With Flow; ISO 2577
0.0070 - 0.010 cm/cm
0.0070 - 0.010 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 76

@Time 15.0 sec
 76

@Time 0.00417 hour
 ASTM D2240
Tensile Strength at Break <= 50.0 MPa
<= 7250 psi
ISO/R527
Elongation at Yield 6.0 %
6.0 %
ISO/R527
Flexural Strength <= 70.0 MPa
<= 10200 psi
ISO 178
Flexural Modulus 2.10 GPa

@Temperature 23.0 °C
 305 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact, Notched 2.00 J/cm²

@Temperature -20.0 °C
 9.52 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
4.40 J/cm²

@Temperature 23.0 °C
 20.9 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 100 °C
212 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C
181 °F
120°C/h; ISO 75/1
Vicat Softening Point 112 °C

@Load 5.001 kg
 234 °F

@Load 11.03 lb
 50°C/h; ISO 306
135 °C

@Load 1.00 kg
 275 °F

@Load 2.21 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 750 °C

@Thickness 2.00 mm
 1380 °F

@Thickness 0.0787 in
 IEC 695-2-1