Polykemi AB SCANAMID 66 A13^ FX30 Nylon 66, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANAMID 66
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANAMID 66 A13^ FX30 Nylon 66, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
ISO 1183
Filler Content 30 %
30 %
±2%; Polykemi
Linear Mold Shrinkage 0.0040 cm/cm
0.0040 in/in
With Flow; ISO 2577
0.010 cm/cm
0.010 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Hardness, Shore D 81

@Time 15.0 sec
81

@Time 0.00417 hour
ASTM D2240
Tensile Strength at Break <= 125 MPa
<= 18100 psi
ISO/R527
Elongation at Break 4.0 %
4.0 %
ISO/R527
Flexural Strength <= 190 MPa
<= 27600 psi
ISO 178
Flexural Modulus 5.60 GPa

@Temperature 23.0 °C
812 ksi

@Temperature 73.4 °F
ISO 178
Charpy Impact, Notched 0.500 J/cm²

@Temperature -20.0 °C
2.38 ft-lb/in²

@Temperature -4.00 °F
ISO 179
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 245 °C
473 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 220 °C

@Load 5.001 kg
>= 428 °F

@Load 11.03 lb
50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
1200 °F

@Thickness 0.0787 in
IEC 695-2-1