Polykemi AB SCANAMID 66 A53^ F43 Nylon 66, Glass Fiber Reinforced, Modified
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | Polykemi AB |
| Trade Name | SCANAMID 66 |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANAMID 66 A53^ F43 Nylon 66, Glass Fiber Reinforced, Modified.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Filler Content | 43 % | 43 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | With Flow; ISO 2577 |
| 0.010 cm/cm | 0.010 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 140 MPa | <= 20300 psi | ISO/R527 |
| Elongation at Break | 10 % | 10 % | ISO/R527 |
| Flexural Strength | <= 220 MPa | <= 31900 psi | ISO 178 |
| Flexural Modulus | 10.4 GPa @Temperature 23.0 °C |
1510 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179 |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| Glow Wire Test | 650 °C @Thickness 2.00 mm |
1200 °F @Thickness 0.0787 in |
IEC 695-2-1 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 223R PC (Europe-Africa-Middle East)
- DuPont™ Surlyn® 1702-1 Zinc Ionomer Resin for Extrusion Coating (discontinued **)
- Haynes Multimet® alloy, 6.15 mm hot-rolled bar, 1185°C heat treatment, rapid air cooled
- Wellman Wellamid® T512-BK 15% Talc/Glass Reinforced, Dimensionally Stable Grade Nylon 6
- Eastman Tenite 350A4861313 Cellulose Acetate Propionate, Clear, Trsp
- Dow Nordel® IP 5565 General Purpose Molding
- Alliance Polymers Viprene™ G55A-32U-BLK Thermoplastic Vulcanizate Elastomer
- Arlon 49090R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Resinlab® EP1238 Acrylic / Epoxy Hybrid Adhesive
- Saint-Gobain Korel® K30-25 Soft Micro-cellular Polyurethane Foam
Copyright © lookpolymers.com All Rights Reserved