Polymer Resources ABS-G30 ABS, 30% Glass Reinforced

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources ABS-G30 ABS, 30% Glass Reinforced.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Acrylonitrile Butadiene Styrene, 30% Glass ReinforcedProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.26 g/cc	1.26 g/cc	ASTM D792
Linear Mold Shrinkage	0.0010 - 0.0020 cm/cm	0.0010 - 0.0020 in/in	ASTM D955
Melt Flow	0.10 - 5.0 g/10 min @Load 3.80 kg, Temperature 230 °C	0.10 - 5.0 g/10 min @Load 8.38 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	96.5 MPa	14000 psi	ASTM D638
Tensile Strength, Yield	96.5 MPa	14000 psi	ASTM D638
Elongation at Yield	1.5 %	1.5 %	ASTM D638
Tensile Modulus	8.96 GPa	1300 ksi	ASTM D638
Flexural Strength	134 MPa	19500 psi	ASTM D790
Flexural Modulus	8.27 GPa	1200 ksi	ASTM D790
Izod Impact, Notched	0.534 J/cm @Temperature 22.8 °C	1.00 ft-lb/in @Temperature 73.0 °F	ASTM D256
Izod Impact, Unnotched	2.67 J/cm @Temperature 22.8 °C	5.00 ft-lb/in @Temperature 73.0 °F	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	113 °C	235 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	107 °C	225 °F	ASTM D648
Flammability, UL94	HB @Thickness 1.59 mm	HB @Thickness 0.0626 in
	HB @Thickness 3.17 mm	HB @Thickness 0.125 in

Processing Properties	Metric	English
Rear Barrel Temperature	199 - 227 °C	390 - 440 °F
Middle Barrel Temperature	210 - 232 °C	410 - 450 °F
Front Barrel Temperature	216 - 238 °C	420 - 460 °F
Melt Temperature	210 - 238 °C	410 - 460 °F
Mold Temperature	60.0 - 82.2 °C	140 - 180 °F
Drying Temperature	79.4 - 85.0 °C	175 - 185 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.001