Polymer Resources ABS-GP-HH General Purpose ABS, High Heat

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources ABS-GP-HH General Purpose ABS, High Heat.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
General Purpose Acrylonitrile Butadiene Styrene, High HeatProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.05 g/cc
1.05 g/cc
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 1.0 - 5.0 g/10 min

@Load 3.80 kg,
Temperature 230 °C
1.0 - 5.0 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D785
Tensile Strength at Break 42.1 MPa
6100 psi
ASTM D638
Tensile Strength, Yield 44.8 MPa
6500 psi
ASTM D638
Elongation at Break 25 %
25 %
ASTM D638
Elongation at Yield 4.5 %
4.5 %
ASTM D638
Tensile Modulus 2.21 GPa
320 ksi
ASTM D638
Flexural Strength 79.3 MPa
11500 psi
ASTM D790
Flexural Modulus 2.48 GPa
360 ksi
ASTM D790
Izod Impact, Notched 0.534 J/cm

@Temperature -40.0 °C
1.00 ft-lb/in

@Temperature -40.0 °F
ASTM D256
1.87 J/cm

@Temperature 22.8 °C
3.50 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Izod Impact, Notched (ISO) 6.30 kJ/m²

@Temperature -30.0 °C
3.00 ft-lb/in²

@Temperature -22.0 °F
ISO 180/1A
13.0 kJ/m²

@Temperature 22.8 °C
6.20 ft-lb/in²

@Temperature 73.0 °F
ISO 180/1A
Charpy Impact, Notched 1.05 J/cm²

@Temperature 22.8 °C
5.00 ft-lb/in²

@Temperature 73.0 °F
ISO 179/1eA
Gardner Impact 22.6 J
16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 102 °C
215 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 90.6 °C
195 °F
ASTM D648
Vicat Softening Point 116 °C
240 °F
120°C/h, 50 N; ASTM D1525
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 193 - 210 °C
380 - 410 °F
Middle Barrel Temperature 216 - 238 °C
420 - 460 °F
Front Barrel Temperature 227 - 254 °C
440 - 490 °F
Melt Temperature 232 - 274 °C
450 - 525 °F
Mold Temperature 48.9 - 82.2 °C
120 - 180 °F
Drying Temperature 82.2 - 93.9 °C
180 - 201 °F
Dry Time 2.00 - 5.00 hour
2.00 - 5.00 hour