Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Polymer Resources ABS-GP1-[color]-3 ABS, General Purpose, UV-stabilized

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources ABS-GP1-[color]-3 ABS, General Purpose, UV-stabilized.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 3.0 - 14 g/10 min
3.0 - 14 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 37.9 MPa
5500 psi
ASTM D638
Tensile Strength, Yield 35.9 MPa
5200 psi
ASTM D638
Flexural Strength 64.1 MPa
9300 psi
ASTM D790
Flexural Modulus 2.28 GPa
330 ksi
ASTM D790
Izod Impact, Notched 2.67 J/cm
5.00 ft-lb/in
ASTM D256
Gardner Impact >= 22.6 J
>= 16.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 87.8 °C
190 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.2 °C
180 °F
ASTM D648
Flammability, UL94 HB
HB
1/8 in
HB
HB
1/16 in
Processing Properties Metric English Comments
Rear Barrel Temperature 188 - 210 °C
370 - 410 °F
Middle Barrel Temperature 204 - 227 °C
400 - 440 °F
Front Barrel Temperature 216 - 238 °C
420 - 460 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 48.9 - 71.1 °C
120 - 160 °F
Drying Temperature 82.2 - 93.3 °C
180 - 200 °F
Dry Time 3 - 4 hour
3 - 4 hour