Polymer Resources PC/ABS-FR2 Flame Retardant PC/ABS Alloy, High Flow

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/ABS-FR2 Flame Retardant PC/ABS Alloy, High Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC/ABS Alloy, Flame Retardant, Higher FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 40 - 60 g/10 min

@Load 5.00 kg,
Temperature 250 °C
40 - 60 g/10 min

@Load 11.0 lb,
Temperature 482 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 56.5 MPa
8200 psi
ASTM D638
Tensile Strength, Yield 57.9 MPa
8400 psi
ASTM D638
Flexural Strength 93.1 MPa
13500 psi
ASTM D790
Flexural Modulus 2.55 GPa
370 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm

@Temperature 22.8 °C
10.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 85.0 °C
185 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.4 °C
175 °F
ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.50 mm
140 °F

@Thickness 0.0591 in
UL 746
60.0 °C

@Thickness 3.00 mm
140 °F

@Thickness 0.118 in
UL 746
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
V-0

@Thickness 0.118 in
Processing Properties Metric English Comments
Rear Barrel Temperature 221 - 254 °C
430 - 490 °F
Middle Barrel Temperature 232 - 266 °C
450 - 510 °F
Front Barrel Temperature 243 - 277 °C
470 - 530 °F
Melt Temperature 246 - 274 °C
475 - 525 °F
Mold Temperature 60.0 - 82.2 °C
140 - 180 °F
Drying Temperature 76.7 - 82.2 °C
170 - 180 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour
Descriptive Properties Value Comments
Vent 0.0015