Polymer Resources PC/TP-GP3 PC/Polyester Alloy

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP
Manufacturer Polymer Resources, LTD
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources PC/TP-GP3 PC/Polyester Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Impact, Superior Chemical ResistanceProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Specific Gravity 1.24 g/cc
1.24 g/cc
ASTM D792
Linear Mold Shrinkage 0.013 - 0.018 cm/cm
0.013 - 0.018 in/in
ASTM D955
Melt Flow 6.0 - 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
6.0 - 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.1 MPa
6400 psi
ASTM D638
Tensile Strength, Yield 46.2 MPa
6700 psi
ASTM D638
Flexural Strength 66.2 MPa
9600 psi
ASTM D790
Flexural Modulus 1.79 GPa
260 ksi
ASTM D790
Izod Impact, Notched 4.81 J/cm

@Temperature -40.0 °C
9.00 ft-lb/in

@Temperature -40.0 °F
ASTM D256
8.01 J/cm

@Temperature 22.8 °C
15.0 ft-lb/in

@Temperature 73.0 °F
ASTM D256
Gardner Impact 36.2 J
26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 116 °C
240 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 76.7 °C
170 °F
ASTM D648
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0626 in
HB

@Thickness 3.17 mm
HB

@Thickness 0.125 in
Processing Properties Metric English Comments
Rear Barrel Temperature 227 - 243 °C
440 - 470 °F
Middle Barrel Temperature 232 - 249 °C
450 - 480 °F
Front Barrel Temperature 238 - 260 °C
460 - 500 °F
Melt Temperature 238 - 260 °C
460 - 500 °F
Mold Temperature 48.9 - 82.2 °C
120 - 180 °F
Drying Temperature 104 - 110 °C
220 - 230 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Descriptive Properties Value Comments
Vent 0.0015