Polymer Resources TP-FR IM PBT, Impact Modified, Flame Retardant, Low Flow

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Impact Grade
Manufacturer Polymer Resources, LTD
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polymer Resources TP-FR IM PBT, Impact Modified, Flame Retardant, Low Flow.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Information provided by Polymer Resources Corporation.
Physical Properties Metric English Comments
Density 1.34 g/cc
0.0484 lb/in³
ASTM D792
Linear Mold Shrinkage 0.010 - 0.014 cm/cm
0.010 - 0.014 in/in
ASTM D955
Melt Flow 3.0 - 9.0 g/10 min
3.0 - 9.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 44.8 MPa
6500 psi
ASTM D638
Tensile Strength, Yield 44.8 MPa
6500 psi
ASTM D638
Flexural Strength 77.57 MPa
11250 psi
ASTM D790
Flexural Modulus 2.00 GPa
290 ksi
ASTM D790
Izod Impact, Notched 5.34 J/cm
10.0 ft-lb/in
ASTM D256
Gardner Impact >= 36.2 J
>= 26.7 ft-lb
ASTM D3029
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 132 °C
270 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.8 °C
190 °F
ASTM D648
Flammability, UL94 V-0
V-0
1/16 in
V-0
V-0
1/8 in
Processing Properties Metric English Comments
Rear Barrel Temperature 238 - 254 °C
460 - 490 °F
Middle Barrel Temperature 243 - 260 °C
470 - 500 °F
Front Barrel Temperature 249 - 266 °C
480 - 510 °F
Melt Temperature 232 - 260 °C
450 - 500 °F
Mold Temperature 43.3 - 82.2 °C
110 - 180 °F
Drying Temperature 116 - 121 °C
240 - 250 °F
Dry Time 3 - 4 hour
3 - 4 hour