Polyram RamTal PM340S4 Acetal, 20% Glass beads Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Glass Bead Filled |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM340S4 Acetal, 20% Glass beads Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass beads reinforced polyacetal for injection molding applicationsInformation provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | DIN 53479 |
| Linear Mold Shrinkage | 0.019 cm/cm | 0.019 in/in | |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C |
20 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM-D638 |
| Elongation at Break | 25 % | 25 % | ASTM-D638 |
| Tensile Modulus | 2.40 GPa | 348 ksi | ASTM-D790 |
| Flexural Strength | 65.0 MPa | 9430 psi | ASTM-D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | DIN 53461 |
| Vicat Softening Point | 165 °C | 329 °F | ASTM-D1525 |