Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite

Category	Polymer , Tape , Thermoplastic , Polypropylene (PP) , Polypropylene with 60% Glass Fiber Filler
Manufacturer	Polystrand, Inc.
Trade Name	ThermoPro™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Fiber Orientation is 0°.Polystrand ThermoPro™ combines continuous E-Glass (ThermoPro-E™) structural reinforcing fibers in either a polyethylene or polypropylene proprietary thermoplastic polymer to form ribbons or tapes. These material forms can be subsequently molded by high temperature processing to create end-use applications including pipe, tanks, liners, automotive, architectural, and a host of other structural industrial and commercial products. Polystrand ThermoPro™ is the result of a quest of more than 15-years to develop structural thermoplastic composites for the international industrial and commercial markets.Information provided by Polystrand.

Physical Properties	Metric	English	Comments
Density	1.50 g/cc	0.0542 lb/in³
Filler Content	60 %	60 %	E-Glass; ASTM D2584
Water Absorption	0.70 %	0.70 %	ASTM D570
Thickness	330 microns	13.0 mil

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	280 MPa	40600 psi	0°; ASTM D3039
Elongation at Break	1.1 %	1.1 %	0°; ASTM D3039
Tensile Modulus	25.1 GPa	3640 ksi	0°; ASTM D3039
Flexural Strength	420 MPa	60900 psi	0°; measured on 0.1" panel molded from tape; ASTM D790
Flexural Modulus	24.1 GPa	3500 ksi	0°; measured on 0.1" panel molded from tape; ASTM D790
Shear Modulus	1.02 GPa	148 ksi	In-Plane G12; ASTM D5379
Shear Strength	24.8 MPa	3600 psi	In-Plane S12; ASTM D5379
	25.5 MPa	3700 psi	Interlaminar S23; ASTM D2344

Thermal Properties	Metric	English	Comments
CTE, linear	9.70 µm/m-°C @Temperature 20.0 °C	5.39 µin/in-°F @Temperature 68.0 °F	Longitudinal; ASTM E228
CTE, linear, Transverse to Flow	64.6 µm/m-°C @Temperature 20.0 °C	35.9 µin/in-°F @Temperature 68.0 °F	ASTM E228
Glass Transition Temp, Tg	165 °C	329 °F	ASTM D3418