Premix Premi-Glas® 1206 LD Fiberglass Reinforced Thermoset SMC

Category Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset
Manufacturer Premix
Trade Name Premi-Glas®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 1206 LD Fiberglass Reinforced Thermoset SMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Premi-Glas® 1206 LD is a fiberglass reinforced thermoset sheet molding compound for transportation or structural and semi-structural applications where good surface appearance, high strength and durability are required in a low density composite.Key features and benefits are:Very good surface profile for highly visible painted surfacedSpecific gravity of 1.5 for weight savings vs. standard compositesAccepts automotive primers and powder in-mold-coatingsExcellent flexural strength and outstanding toughnessDesigned for compression molding in matched metal die molds.Information provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
Filler Content 38 %
38 %
Glass, weight fraction; Premix washout
Linear Mold Shrinkage 0.00025 cm/cm
0.00025 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 100 MPa
14500 psi
ASTM D638
Elongation at Break 1.9 %
1.9 %
ASTM D638
Tensile Modulus 8.50 GPa
1230 ksi
ASTM D638
Flexural Strength 220 MPa
31900 psi
ASTM D790
Flexural Modulus 8.00 GPa
1160 ksi
ASTM D790
Izod Impact, Notched 11.0 J/cm
20.6 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.0 J/cm
28.1 ft-lb/in
ASTM D4812
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure