Premix Premi-Glas® 2206-22 CR-SX Fiberglass Reinforced Thermoset SMC

Category Polymer , Thermoset , Composite SMC , Filled/Reinforced Thermoset
Manufacturer Premix
Trade Name Premi-Glas®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Premi-Glas® 2206-22 CR-SX Fiberglass Reinforced Thermoset SMC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Premi-Glas® 2206-22 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant and HVAC applications.Key features and benefits are:Non-Halogen FR technology for regulatory compliancePigmentable for molded-in color; best appearance with mold textureSuitable for outdoor use in applications involving UV exposure and water immersion in accordance with UL746C (f1), file E42524Designed for compression molding in matched metal die molds.Information provided by Premix.
Physical Properties Metric English Comments
Specific Gravity 1.75 - 1.85 g/cc
1.75 - 1.85 g/cc
Linear Mold Shrinkage 0.0010 - 0.0025 cm/cm
0.0010 - 0.0025 in/in
Polymerization Shrinkage
Mechanical Properties Metric English Comments
Tensile Strength 40.0 MPa
5800 psi
ASTM D638
Tensile Modulus 9.00 GPa
1310 ksi
ASTM D638
Flexural Strength 115 MPa
16700 psi
ASTM D790
Flexural Modulus 9.00 GPa
1310 ksi
ASTM D790
Poissons Ratio 0.30
0.30
Shear Modulus 3.50 GPa
508 ksi
Calculated
Izod Impact, Notched 4.90 J/cm
9.18 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.50 J/cm
12.2 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 20.0 µm/m-°C
11.1 µin/in-°F
Z Direction
CTE, linear, Transverse to Flow 15.0 µm/m-°C
8.33 µin/in-°F
XY Direction
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
UL RTI, Electrical 130 °C
266 °F
UL 746C
UL RTI, Mechanical with Impact 130 °C
266 °F
UL 746C
UL RTI, Mechanical without Impact 130 °C
266 °F
UL 746C
Flammability, UL94 V-0

@Thickness 2.30 mm
V-0

@Thickness 0.0906 in
5VB

@Thickness 2.30 mm
5VB

@Thickness 0.0906 in
Electrical Properties Metric English Comments
Dielectric Strength 18.0 kV/mm
457 kV/in
ASTM D149
Arc Resistance >= 180 sec
>= 180 sec
ASTM D495
Comparative Tracking Index 600 V
600 V
ASTM D2303
Processing Properties Metric English Comments
Processing Temperature 150 °C
302 °F
Compression Molding
Clamp Pressure 3.45 - 6.89 MPa
500 - 1000 psi
Molding Pressure