Premix Premi-Ject® 1102H Fiberglass Reinforced Thermoset BMC

Category	Polymer , Thermoset , Filled/Reinforced Thermoset
Manufacturer	Premix
Trade Name	Premi-Ject®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Premix Premi-Ject® 1102H Fiberglass Reinforced Thermoset BMC.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Premi-Ject® 1102H is a fiberglass reinforced thermoset bulk molding compound for coil encapsulation applications.Key features and benefits are:Designed with unique flow properties to encapsulate coil windingsExcellent transfer and injection process capabilities in multi-cavity toolsRecognized by Underwriters Laboratories, File #E42524May be extruded for high output transfer moldingStandard colors are blue and blackDesigned for transfer or injection molding in matched metal die molds.Information provided by Premix.

Physical Properties	Metric	English	Comments
Specific Gravity	1.85 - 1.95 g/cc	1.85 - 1.95 g/cc
Linear Mold Shrinkage	0.00050 - 0.0015 cm/cm	0.00050 - 0.0015 in/in	Polymerization Shrinkage

Mechanical Properties	Metric	English	Comments
Tensile Strength	26.0 MPa	3770 psi	ASTM D638
Elongation at Break	0.40 %	0.40 %	ASTM D638
Tensile Modulus	9.00 GPa	1310 ksi	ASTM D638
Flexural Strength	68.0 MPa	9860 psi	ASTM D790
Flexural Modulus	9.00 GPa	1310 ksi	ASTM D790
Poissons Ratio	0.30	0.30
Shear Modulus	3.50 GPa	508 ksi	Calculated
Izod Impact, Notched	3.75 J/cm	7.03 ft-lb/in	ASTM D256
Izod Impact, Unnotched	4.25 J/cm	7.96 ft-lb/in	ASTM D4812

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	35.0 µm/m-°C	19.4 µin/in-°F	Z Direction
CTE, linear, Transverse to Flow	25.0 µm/m-°C	13.9 µin/in-°F	XY Direction
Thermal Conductivity	0.300 W/m-K	2.08 BTU-in/hr-ft²-°F
Deflection Temperature at 1.8 MPa (264 psi)	>= 200 °C	>= 392 °F	ASTM D792
UL RTI, Electrical	130 °C	266 °F	UL 746C
UL RTI, Mechanical with Impact	130 °C	266 °F	UL 746C
UL RTI, Mechanical without Impact	130 °C	266 °F	UL 746C
Flammability, UL94	HB @Thickness 3.20 mm	HB @Thickness 0.126 in

Electrical Properties	Metric	English	Comments
Dielectric Strength	13.0 kV/mm	330 kV/in	ASTM D149
Arc Resistance	188 sec	188 sec	ASTM D495

Processing Properties	Metric	English	Comments
Processing Temperature	150 °C	302 °F	Transfer or Injection Molding
Clamp Pressure	3.45 - 6.89 MPa	500 - 1000 psi	Molding Pressure