Premix Thermoplastics PRE-ELEC® CP 1315 (discontinued **)
| Category | Polymer , Thermoplastic , Polyolefin |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Premix Thermoplastics PRE-ELEC® CP 1315
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PRE-ELEC CP 1315 is a conductive thermoplastic compound based on a polyolefin copolymer. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC CP 1315 has excellent mechanical properties and is easy to extrude or injection mould.Typical applications include flexible extruded profiles and tubes and flexible injection molded parts. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Linear Mold Shrinkage | 0.014 - 0.018 cm/cm | 0.014 - 0.018 in/in | ISO 294-4 |
| Melt Flow | 5.0 g/10 min @Load 5.00 kg, Temperature 190 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| High Load Melt Index | 25 g/10 min @Load 21.6 kg, Temperature 190 °C |
25 g/10 min @Load 47.6 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 97 | 97 | ISO 868 |
| Hardness, Shore D | 45 | 45 | ISO 868 |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ISO 527 |
| Elongation at Break | 150 % | 150 % | ISO 527 |
| Modulus of Elasticity | 0.200 GPa | 29.0 ksi | ISO 178 |
| Izod Impact, Notched | NB @Thickness 4.00 mm, Temperature 23.0 °C |
NB @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Izod Impact, Unnotched | NB @Thickness 4.00 mm, Temperature 23.0 °C |
NB @Thickness 0.157 in, Temperature 73.4 °F |
ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ISO 75/Method Bf |
| Vicat Softening Point | 73.0 °C | 163 °F | Rate A; ISO 306/A50 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | <= 10000 ohm-cm | <= 10000 ohm-cm | ISO D-257 |
| Surface Resistance | <= 1e+05 | <= 1e+05 | ISO D-257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 180 °C | 356 °F | Zone 1; Cylinder |
| 180 °C | 356 °F | Zone 2; Cylinder | |
| 190 °C | 374 °F | Zone 3; Cylinder | |
| 190 °C | 374 °F | Zone 4; Cylinder | |
| 200 °C | 392 °F | Zone 5; Cylinder | |
| 200 °C | 392 °F | Zone 6; Cylinder | |
| Die Temperature | 190 °C | 374 °F | Zone 3 |
| 200 °C | 392 °F | Zone 4 | |
| 200 °C | 392 °F | Zone 1 | |
| 200 °C | 392 °F | Zone 2 | |
| 200 °C | 392 °F | Zone 5 | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Roll Temperature | 50.0 °C | 122 °F | 3rd Roll |
| 60.0 °C | 140 °F | 2nd Roll | |
| 70.0 °C | 158 °F | 1st Roll | |
| Drying Temperature | 60.0 °C @Time >=10800 sec |
140 °F @Time >=3.00 hour |
If stored for longer than 1 year |
| Moisture Content | <= 0.15 % | <= 0.15 % | When Produced |
| Injection Pressure | 60.00 MPa | 8702 psi | |
| Shelf Life | 12.0 Month | 12.0 Month | Normal Storing Conditions |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Granule | |
| Color | Black | |
| Injection Speed | Moderate |