Premix Thermoplastics PRE-ELEC® PC 1431

Category Polymer , Film , Thermoplastic , Polycarbonate (PC)
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PC 1431.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC PC 1431 is a conductive thermoplastic compound based on polycarbonate. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PC 1431 has excellent mechanical properties and is easy to extrude. PRE-ELEC PC 1431 can also be injection molded.Typical applications include extruded sheets for monolayer microchip carrier tape.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
Thickness 406 microns
16.0 mil
Linear Mold Shrinkage <= 0.0060 cm/cm
<= 0.0060 in/in
4 mm thick, 10.0 mm wide molded rod; ISO 294-4
Melt Flow 1.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
1.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ISO 1133
4.0 g/10 min

@Load 2.16 kg,
Temperature 300 °C
4.0 g/10 min

@Load 4.76 lb,
Temperature 572 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 85
85
4.0 mm thick, 10.0 mm wide molded rod; ISO 868
Film Tensile Strength at Yield, MD 50.0 MPa
7250 psi
ISO 527
Film Tensile Strength at Yield, TD 45.0 MPa
6530 psi
ISO 527
Film Elongation at Break, MD 20 %
20 %
ISO 527
Film Elongation at Break, TD 15 %
15 %
ISO 527
Film Elongation at Yield, MD 6.0 %
6.0 %
ISO 527
Film Elongation at Yield, TD 6.0 %
6.0 %
ISO 527
Modulus of Elasticity 2.50 GPa
363 ksi
4 mm thick;10.0 mm wide molded rod; ISO 178
Izod Impact, Notched 0.800 J/cm

@Thickness 4.00 mm,
Temperature -20.0 °C
1.50 ft-lb/in

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
1.75 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
3.28 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched 8.80 J/cm

@Thickness 4.00 mm,
Temperature -20.0 °C
16.5 ft-lb/in

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
8.80 J/cm

@Thickness 4.00 mm,
Temperature 23.0 °C
16.5 ft-lb/in

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Film Tensile Strength at Break, MD 47.0 MPa
6820 psi
ISO 527
Film Tensile Strength at Break, TD 44.0 MPa
6380 psi
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 134 °C
273 °F
4 mm thick;10.0 mm wide molded rod; ISO 75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 120 °C
248 °F
4 mm thick;10.0 mm wide molded rod; ISO 75/Method Af
Vicat Softening Point 140 °C
284 °F
Rate B; 4 mm thick;10.0 mm wide molded rod; ISO 306/B50
147 °C
297 °F
Rate A; 4 mm thick;10.0 mm wide molded rod; ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 1e+05
<= 1e+05
400 um thick sheet; ISO D-257
Surface Resistance <= 1.00e+7 ohm
<= 1.00e+7 ohm
400 um thick sheet; ISO D-257
Processing Properties Metric English Comments
Middle Barrel Temperature 250 °C
482 °F
Zone 1; Cylinder
260 °C
500 °F
Zone 4; Cylinder
260 °C
500 °F
Zone 2; Cylinder
260 °C
500 °F
Zone 3; Cylinder
270 °C
518 °F
Zone 5; Cylinder
270 °C
518 °F
Zone 6; Cylinder
Die Temperature 260 °C
500 °F
Zone 3
280 °C
536 °F
Zone 4
280 °C
536 °F
Zone 1
280 °C
536 °F
Zone 5
280 °C
536 °F
Zone 2
Roll Temperature 70.0 °C
158 °F
3rd Roll
80.0 °C
176 °F
2nd Roll
90.0 °C
194 °F
1st Roll
Drying Temperature 100 - 120 °C

@Time 7200 - 14400 sec
212 - 248 °F

@Time 2.00 - 4.00 hour
Pre-drying
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Black