Premix Thermoplastics PRE-ELEC® PE 1294

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PE 1294.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC PE 1294 is a conductive thermoplastic compound based on PE-HD. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC PE 1294has excellent mechanical properties and is easy to injection mould, extrude and blow mould. Typical applications include injection molded pallets, crates, extruded sheets for thermoforming and linings and blow molded drums and canisters. Test Specimen - 4.0 mm thick, 10.0 mm wide molded rod.Information provided by Premix Thermoplastics Inc.
Physical Properties Metric English Comments
Density 1.01 g/cc
0.0365 lb/in³
Linear Mold Shrinkage 0.015 - 0.025 cm/cm
0.015 - 0.025 in/in
ISO 294-4
Melt Flow 2.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
2.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
20 g/10 min

@Load 10.0 kg,
Temperature 190 °C
20 g/10 min

@Load 22.0 lb,
Temperature 374 °F
ISO 1133
High Load Melt Index 70 g/10 min

@Load 21.6 kg,
Temperature 190 °C
70 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 66
66
ISO 868
Tensile Strength, Ultimate 12.0 MPa
1740 psi
ISO 527
Tensile Strength, Yield 22.0 MPa
3190 psi
ISO 527
Elongation at Break 180 %
180 %
ISO 527
Elongation at Yield 15 %
15 %
ISO 527
Modulus of Elasticity 0.810 GPa
117 ksi
ISO 178
Izod Impact, Notched NB

@Thickness 4.00 mm,
Temperature -20.0 °C
NB

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched NB

@Thickness 4.00 mm,
Temperature -20.0 °C
NB

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 65.0 °C
149 °F
ISO 75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 39.0 °C
102 °F
ISO 75/Method Af
Vicat Softening Point 60.0 °C
140 °F
Rate B; ISO 306/B50
125 °C
257 °F
Rate A; ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 10000 ohm-cm
<= 10000 ohm-cm
ISO D-257
Surface Resistance <= 1e+05
<= 1e+05
ISO D-257
Processing Properties Metric English Comments
Middle Barrel Temperature 200 °C
392 °F
Zone 1; Cylinder
210 °C
410 °F
Zone 2; Cylinder
220 °C
428 °F
Zone 3; Cylinder
220 °C
428 °F
Zone 4; Cylinder
230 °C
446 °F
Zone 5; Cylinder
230 °C
446 °F
Zone 6; Cylinder
Die Temperature 220 °C
428 °F
Zone 3
230 °C
446 °F
Zone 2
230 °C
446 °F
Zone 4
240 °C
464 °F
Zone 5
240 °C
464 °F
Zone 1
Melt Temperature 180 - 250 °C
356 - 482 °F
Mold Temperature 30.0 - 70.0 °C
86.0 - 158 °F
Roll Temperature 50.0 °C
122 °F
3rd Roll
60.0 °C
140 °F
2nd Roll
70.0 °C
158 °F
1st Roll
Drying Temperature 80.0 °C

@Time 7200 - 14400 sec
176 °F

@Time 2.00 - 4.00 hour
Pre-drying in a dehumidifier
Moisture Content <= 0.15 %
<= 0.15 %
When Produced
Injection Pressure 75.2 - 120 MPa
10900 - 17400 psi
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Appearance Granule
Color Black
Injection Speed Moderate
Post Pressure, psi 5800 - 8700