Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with Carbon Black Filler
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PP 1396 Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PP 1396 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1396 has excellent mechanical properties and is easy to extrude. Applications: Extrusion of conductive PP-tape.Processing: PRE-ELEC® PP 1396 compound can be extruded in the machines using normal processing conditions as with polypropylene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.012 - 0.017 cm/cm
0.012 - 0.017 in/in
ISO 294-4
Melt Flow 3.0 g/10 min

@Load 5.00 kg,
Temperature 230 °C
3.0 g/10 min

@Load 11.0 lb,
Temperature 446 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore A 98
98
ISO 868
Hardness, Shore D 73
73
ISO 868
Film Elongation at Break, MD 4.0 %

@Thickness 0.400 mm
4.0 %

@Thickness 0.0157 in
ISO 527
Flexural Modulus 2.50 GPa
363 ksi
ISO 178
Izod Impact, Notched (ISO) 2.00 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
0.952 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) 18.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
8.57 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Charpy Impact Unnotched 1.40 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
6.66 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.300 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
1.43 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Film Tensile Strength at Break, MD 33.0 MPa

@Thickness 0.400 mm
4790 psi

@Thickness 0.0157 in
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 108 °C
226 °F
75/Method Bf
Deflection Temperature at 1.8 MPa (264 psi) 64.0 °C
147 °F
75/Method Af
Vicat Softening Point 155 °C
311 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 10 ohm-cm

@Thickness 0.400 mm
<= 10 ohm-cm

@Thickness 0.0157 in
ISO D-257
Surface Resistance <= 1.00e+6 ohm
<= 1.00e+6 ohm
5 x stretched tape; ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 250 °C
482 °F
Die
250 °C
482 °F
Cylinder
Zone 2 250 °C
482 °F
Die
260 °C
500 °F
Cylinder
Zone 3 250 °C
482 °F
Die
270 °C
518 °F
Cylinder
Zone 4 250 °C
482 °F
Die
270 °C
518 °F
Cylinder
Zone 5 250 °C
482 °F
Die
270 °C
518 °F
Cylinder
Roll Temperature 90.0 °C
194 °F
1st Roll
100 °C
212 °F
2nd Roll
100 °C
212 °F
3rd Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 2 - 4 hour
2 - 4 hour
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions