Premix Thermoplastics PRE-ELEC® PS 1331 Carbon Black Filled Conductive Thermoplastic Compound

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Carbon Black Filled
Manufacturer Premix Thermoplastics Inc.
Trade Name PRE-ELEC®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Premix Thermoplastics PRE-ELEC® PS 1331 Carbon Black Filled Conductive Thermoplastic Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PRE-ELEC® PS 1331 is a carbon black filled conductive thermoplastic compound based on polystyrene. In addition to a low electrical resistivity PRE-ELEC® PS 1331 has excellent mechanical properties and is easy to extrude. The chemical purity of PRE-ELEC® PS 1331 is very good. Moisture pick up of PRE-ELEC® PS 1331 is minimal so the pre-drying of the sheets is not always necessary. PRE-ELEC® PS 1331 is developed for microchip carrier tape applications. It is also suitable for co-extruded tape.Processing: PRE-ELEC® PS 1331 compound can be extruded in the machines using normal processing conditions as with polystyrene.Test Specimen: 10[mm] wide moulded rodInformation from Premix OY
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
Thickness 102 microns
4.00 mil
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ISO 294-4
Melt Flow 1.8 g/10 min

@Load 5.00 kg,
Temperature 200 °C
1.8 g/10 min

@Load 11.0 lb,
Temperature 392 °F
ISO 1133
60 g/10 min

@Load 21.6 kg,
Temperature 200 °C
60 g/10 min

@Load 47.6 lb,
Temperature 392 °F
ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
ISO 868
Film Tensile Strength at Yield, MD 33.0 MPa

@Thickness 0.400 mm
4790 psi

@Thickness 0.0157 in
ISO 527
Film Tensile Strength at Yield, TD 39.0 MPa

@Thickness 0.400 mm
5660 psi

@Thickness 0.0157 in
ISO 527
Film Elongation at Break, MD 66 %

@Thickness 0.400 mm
66 %

@Thickness 0.0157 in
ISO 527
Film Elongation at Break, TD 34 %

@Thickness 0.400 mm
34 %

@Thickness 0.0157 in
ISO 527
Film Elongation at Yield, MD 5.0 %

@Thickness 0.400 mm
5.0 %

@Thickness 0.0157 in
ISO 527
Film Elongation at Yield, TD 8.0 %

@Thickness 0.400 mm
8.0 %

@Thickness 0.0157 in
ISO 527
Flexural Modulus 1.50 GPa
218 ksi
ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Thickness 4.00 mm,
Temperature -20.0 °C
2.86 ft-lb/in²

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
20.0 kJ/m²

@Thickness 4.00 mm,
Temperature 23.0 °C
9.52 ft-lb/in²

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
Izod Impact, Unnotched (ISO) NB

@Thickness 4.00 mm,
Temperature 23.0 °C
NB

@Thickness 0.157 in,
Temperature 73.4 °F
ISO 180
NB

@Thickness 4.00 mm,
Temperature -20.0 °C
NB

@Thickness 0.157 in,
Temperature -4.00 °F
ISO 180
Charpy Impact Unnotched 6.50 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
30.9 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
NB

@Thickness 102 mm,
Temperature 23.0 °C
NB

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Charpy Impact, Notched 0.800 J/cm²

@Thickness 102 mm,
Temperature -20.0 °C
3.81 ft-lb/in²

@Thickness 4.00 in,
Temperature -4.00 °F
ISO 179
2.50 J/cm²

@Thickness 102 mm,
Temperature 23.0 °C
11.9 ft-lb/in²

@Thickness 4.00 in,
Temperature 73.4 °F
ISO 179
Film Tensile Strength at Break, MD 31.0 MPa

@Thickness 0.400 mm
4500 psi

@Thickness 0.0157 in
ISO 527
Film Tensile Strength at Break, TD 40.0 MPa

@Thickness 0.400 mm
5800 psi

@Thickness 0.0157 in
ISO 527
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
75/Method Bf
Vicat Softening Point 97.0 °C
207 °F
ISO 306/A50
Electrical Properties Metric English Comments
Volume Resistivity <= 10000 ohm-cm

@Thickness 0.400 mm
<= 10000 ohm-cm

@Thickness 0.0157 in
ISO D-257
Surface Resistance <= 1.00e+6 ohm

@Thickness 0.400 mm
<= 1.00e+6 ohm

@Thickness 0.0157 in
ISO IEC 61340-5-1
Processing Properties Metric English Comments
Zone 1 200 °C
392 °F
Cylinder
220 °C
428 °F
Die
Zone 2 210 °C
410 °F
Cylinder
220 °C
428 °F
Die
Zone 3 210 °C
410 °F
Die
210 °C
410 °F
Cylinder
Zone 4 220 °C
428 °F
Die
220 °C
428 °F
Cylinder
Zone 5 220 °C
428 °F
Die
220 °C
428 °F
Cylinder
Roll Temperature 60.0 °C
140 °F
3rd Roll
80.0 °C
176 °F
2nd Roll
90.0 °C
194 °F
1st Roll
Drying Temperature 60.0 - 80.0 °C
140 - 176 °F
Pre-drying
Dry Time 3 - 4 hour
3 - 4 hour
Shelf Life 12.0 Month
12.0 Month
Normal Storing Conditions
Descriptive Properties Value Comments
Bending Strength, MD (cycles) >1000
ISO 5626
Bending Strength, TD (cycles) >1000
ISO 5626