Proto3000 ABS-M30i Fused Deposition Modeling Polymer

Category Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer
Manufacturer Proto3000
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Proto3000 ABS-M30i Fused Deposition Modeling Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: ABS-M30i is a high strength material well suited for the medical, pharmaceutical and food packaging industries. Parts manufactured with ABS-M30i material are biocompatible (ISO 10993 certified) and can be gamma or EtO sterilized. When combined with Fortus 3D Production Systems, ABS-M30i gives you biocompatible Real Parts™ with excellent mechanical properties that are well suited for conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts.Available Colors: IvoryInformation provided by Proto3000 for their protoyping engineering services.
Physical Properties Metric English Comments
Density 1.04 g/cc
0.0376 lb/in³
ASTM D792
Mechanical Properties Metric English Comments
Hardness, Rockwell R 109.5
109.5
ASTM D785
Tensile Strength at Break 36.0 MPa
5220 psi
Type 1, 2"/min; ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
52 %
52 %
Flexural Elongation; ASTM D790
Tensile Modulus 2.413 GPa
350.0 ksi
ASTM D638
Flexural Strength 61.0 MPa
8850 psi
Method 1, 0.05"/min; ASTM D790
Flexural Modulus 2.317 GPa
336.1 ksi
ASTM D790
Izod Impact, Notched 1.39 J/cm
2.60 ft-lb/in
Method A; ASTM D256
Izod Impact, Unnotched 2.83 J/cm
5.30 ft-lb/in
Method A; ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.2 µm/m-°C

@Temperature -40.0 - 100 °C
45.7 µin/in-°F

@Temperature -40.0 - 212 °F
ASTM E831
CTE, linear, Transverse to Flow 84.6 µm/m-°C

@Temperature -40.0 - 100 °C
47.0 µin/in-°F

@Temperature -40.0 - 212 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 96.0 °C

@Thickness 0.125 mm
205 °F

@Thickness 0.00492 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 82.0 °C

@Thickness 0.125 mm
180 °F

@Thickness 0.00492 in
unannealed; ASTM D648
Vicat Softening Point 99.0 °C
210 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 108 °C
226 °F
DAM (SSYS)
Flammability, UL94 HB

@Thickness 0.850 mm
HB

@Thickness 0.0335 in
Electrical Properties Metric English Comments
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 60112