Proto3000 ABSi Fused Deposition Modeling Polymer
| Category | Polymer , Rapid Prototyping Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | Proto3000 |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Proto3000 ABSi Fused Deposition Modeling Polymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Stratasys ABSi is an ideal material for conceptual modeling, functional prototyping and direct digital manufacturing. Its strength is superior to standard Stratasys ABS, and the translucent nature of ABSi beneficial for monitoring material flow and light transmission, most commonly used for medical and automotive applications. ABSi gives you Real Parts™ that are visually unique, dimensionally accurate, durable and hold their shape over timeAvailable Colors: Translucent Natural, Translucent Amber and Translucent RedInformation provided by Proto3000 for their protoyping engineering services.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength at Break | 37.0 MPa | 5370 psi | Type 1, 2"/min; ASTM D638 |
| Elongation at Break | 4.4 % | 4.4 % | ASTM D638 |
| <= 80 % | <= 80 % | Flexural Elongation; ASTM D790 | |
| Tensile Modulus | 1.915 GPa | 277.7 ksi | ASTM D638 |
| Flexural Strength | 62.0 MPa | 8990 psi | Method 1, 0.05"/min; ASTM D790 |
| Flexural Modulus | 1.917 GPa | 278.0 ksi | ASTM D790 |
| Izod Impact, Notched | 0.964 J/cm | 1.81 ft-lb/in | Method A; ASTM D256 |
| Izod Impact, Unnotched | 1.911 J/cm | 3.580 ft-lb/in | Method A; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 121 µm/m-°C | 67.2 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 0.125 mm |
187 °F @Thickness 0.00492 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.0 °C @Thickness 0.125 mm |
163 °F @Thickness 0.00492 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 116 °C | 241 °F | DAM (SSYS) |
| Flammability, UL94 | HB | HB |