Proto3000 Accura® Amethyst™ Material for use with Viper™ SLA® systems
| Category | Polymer , Rapid Prototyping Polymer |
| Manufacturer | Proto3000 |
| Trade Name | Accura® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Proto3000 Accura® Amethyst™ Material for use with Viper™ SLA® systems.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Optimized for the rapid and automated production of patterns and master molds for jewelry manufacturing. FEATURES:Outstanding accuracyExceptional detailHigh thermal resistanceDeep purple colorLow ash formulationBENEFITS:Parts are accurately produced in X, Y and ZSmall details are faithfully reproducedPatterns are compatible with high temperature rubber molding operationsProduces parts in a high contract color for easyMaterial can be burned out for direct castingAPPLICATIONS:Patterns for use with low and high vulcanizing rubber moldingHigh resolution concept modelsInformation provided by Proto3000 for their protoyping engineering services.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | Liquid |
| 1.23 g/cc | 0.0444 lb/in³ | Solid | |
| Viscosity | 350 cP @Temperature 30.0 °C |
350 cP @Temperature 86.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 87 | 87 | |
| Tensile Strength at Break | 22.0 - 38.0 MPa | 3190 - 5510 psi | ASTM D638 |
| Elongation at Break | 0.56 - 1.04 % | 0.56 - 1.04 % | ASTM D638 |
| Tensile Modulus | 3.514 - 3.996 GPa | 509.7 - 579.6 ksi | ASTM D638 |
| Flexural Strength | 87.0 - 125 MPa | 12600 - 18100 psi | ASTM D790 |
| Flexural Modulus | 3.652 - 3.721 GPa | 529.7 - 539.7 ksi | ASTM D790 |
| Izod Impact, Notched | 0.0900 - 0.120 J/cm | 0.169 - 0.225 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 57.0 µm/m-°C @Temperature 0.000 - 20.0 °C |
31.7 µin/in-°F @Temperature 32.0 - 68.0 °F |
T<Tg; ASTM E831-93 |
| 133 µm/m-°C @Temperature 90.0 - 150 °C |
73.9 µin/in-°F @Temperature 194 - 302 °F |
T>Tg; ASTM E831-93 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ASTM D648 |
| Glass Transition Temp, Tg | 103 °C | 217 °F | DMA, E" |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Purple | |
| Critical Exposure (Ec) | 14.4 mJ/cm2 | |
| Penetration Depth (Dp) | 3.7 mils |