Proto3000 Objet VeroGray FullCure850 Rigid Opaque Prototyping Polymer

Category Polymer , Rapid Prototyping Polymer
Manufacturer Proto3000
Trade Name Objet
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Proto3000 Objet VeroGray FullCure850 Rigid Opaque Prototyping Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Objet’s FullCure® Materials family of proprietary acrylic-based photopolymer materials enables Objet users to create highly accurate, finely detailed 3D models and parts for a wide range of Rapid Prototyping and Rapid Manufacturing applications. Vero Family: Opaque rigid materials offering toughness, dimensional stability and great detail visualizationFields of Use: Consumer electronics, Toy, Telecommunications, Computers and Architecture fields, Jewelry applicationsInformation provided by Proto3000 for their protoyping engineering services.
Physical Properties Metric English Comments
Density 1.17 - 1.18 g/cc
0.0423 - 0.0426 lb/in³
Polymerized; ASTM D792
Water Absorption 1.1 - 1.5 %

@Time 86400 sec
1.1 - 1.5 %

@Time 24.0 hour
ASTM D570-98
Ash 0.23 - 0.26 %
0.23 - 0.26 %
USP281
Mechanical Properties Metric English Comments
Hardness, Rockwell M 73 - 76
73 - 76
Hardness, Shore D 83 - 86
83 - 86
Tensile Strength at Break 50.0 - 65.0 MPa
7250 - 9430 psi
ASTM D638-03
Elongation at Break 10 - 25 %
10 - 25 %
ASTM D638-05
Modulus of Elasticity 2.00 - 3.00 GPa
290 - 435 ksi
ASTM D638-04
Flexural Strength 75.0 - 110 MPa
10900 - 16000 psi
ASTM D790-03
Flexural Modulus 2.20 - 3.20 GPa
319 - 464 ksi
ASTM D790-04
Izod Impact, Notched 0.200 - 0.300 J/cm
0.375 - 0.562 ft-lb/in
ASTM D256-06
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 45.0 - 50.0 °C
113 - 122 °F
ASTM D648-06
Deflection Temperature at 1.8 MPa (264 psi) 45.0 - 50.0 °C
113 - 122 °F
ASTM D648-07
Glass Transition Temp, Tg 52.0 - 54.0 °C
126 - 129 °F
DMA, E