RTP Company RTP 104 CC FR A Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - Non PBB/PBDE
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 104 CC FR A Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - Non PBB/PBDE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D 792 |
| Water Absorption | 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0015 - 0.0030 in/in @Thickness 0.125 in |
ASTM D 955 |
| Melt Flow | 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D 785 |
| Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D 638 |
| Elongation at Break | 2.5 - 4.0 % | 2.5 - 4.0 % | ASTM D 638 |
| Tensile Modulus | 7.93 GPa | 1150 ksi | ASTM D 638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D 790 |
| Flexural Modulus | 6.55 GPa | 950 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D 4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ESD STM11.11 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
Dry; ASTM D 150 |
| Dielectric Strength | 23.6 kV/mm | 600 kV/in | short term, in oil; ASTM D 149 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
Dry; ASTM D 150 |
| Arc Resistance | 85 sec | 85 sec | ASTM D 495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 191 - 232 °C | 375 - 450 °F | |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | |
| Drying Temperature | 79.4 °C @Time 7200 sec |
175 °F @Time 2.00 hour |
|
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 502UV (NT) Synthetic Oil
- Kingfa HF-626 Flame Retardant ABS
- KYDEX® 6565 Acrylic/PVC Thermoplastic Sheet
- Multibase Multi-Flex® A 0840 Black TPE Thermoplastic Elastomer
- SABIC Innovative Plastics Ultem AUT230M PEI
- RTP Company RTP 152 HF Polypropylene (PP), High Flow - Flame Retardant - UL94 V-2
- Hexcel® HexPly® M48 180°C/356°F Curing Epoxy Matrix, M48/42%/G1094/1000
- EMS-Griltech Griltex® D 1655E Copolyester Hotmelt Adhesive (Technical Applications)
- Eurotec® Tecodur® PB70 GR20 NL PBT 20% glass fiber reinforced
- AK Steel CL 2/ SAE J1392 045 XLK, Grade 45 Cold Rolled Carbon Steel, High Strength Low Alloy Steel (HSLAS)
Copyright © lookpolymers.com All Rights Reserved