- RTP Company RTP 105 CC FR Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - UL94 V-0
RTP Company RTP 105 CC FR Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - UL94 V-0
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | RTP Company |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 105 CC FR Polypropylene (PP), Glass Fiber - Chemically Coupled - Flame Retardant - UL94 V-0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.47 g/cc | 1.47 g/cc | ASTM D 792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hrs @ 23°C; ASTM D 570 |
| Linear Mold Shrinkage | 0.0015 - 0.0030 cm/cm @Thickness 3.17 mm |
0.0015 - 0.0030 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 2.0 - 4.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
2.0 - 4.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 105 | 105 | ASTM D 785 |
| Tensile Strength at Break | 68.9 MPa | 10000 psi | ASTM D 638 |
| Elongation at Break | 2.5 - 4.0 % | 2.5 - 4.0 % | ASTM D 638 |
| Tensile Modulus | 7.93 GPa | 1150 ksi | ASTM D 638 |
| Flexural Strength | 114 MPa | 16500 psi | ASTM D 790 |
| Flexural Modulus | 6.21 GPa | 900 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
D 256 |
| Izod Impact, Unnotched | 5.34 J/cm @Thickness 3.17 mm |
10.0 ft-lb/in @Thickness 0.125 in |
ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 157 °C | 315 °F | ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D 648 |
| Flammability, UL94 | V-0 @Thickness 0.7937 mm |
V-0 @Thickness 0.03125 in |
|
| V-0 @Thickness 3.17 mm |
V-0 @Thickness 0.125 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
Dry; ASTM D 150 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Short Term; in oil; ASTM D 149 |
| Dissipation Factor | 0.0030 @Frequency 1.00e+6 Hz |
0.0030 @Frequency 1.00e+6 Hz |
Dry; ASTM D 150 |
| Arc Resistance | 85 sec | 85 sec | ASTM D 495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 191 - 232 °C | 375 - 450 °F | |
| Mold Temperature | 32.2 - 65.6 °C | 90.0 - 150 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 hour | 2 hour | |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi |
Users viewing this material also viewed the following:
- Ovation Polymers SOFTAPLAS™ S 75A Thermoplastic Elastomer
- Schott N-ZK7 Glass
- Sharadaa Ceramics REFINSUL 11 Insulating Castables Medium/High Purity
- Techmer ES Luriblend® PA6 TL15 Nylon 6
- Saint-Gobain Chemfab® 3 High-Performance PTFE-Coated Glass
- Samsung Cheil Industries Starex® GA-4025 ABS, 25% Glass Filled
- Solvay RHODACAL® N Surfactant
- Chosun Refractories HL-18 Special Insulating Firebrick
- BASF Ultramid® KR 4355 G10 BK 23215 50% Glass Filled PA6/6T (Conditioned)
- Celanese GUR 4150 PE-UHMW, Unfilled
Copyright © lookpolymers.com All Rights Reserved