RTP Company RTP 1381 TFE 20 Polyphenylene Sulfide (PPS) Carbon Fiber - PTFE Lubricated

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with Carbon Fiber + PTFE Filler
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1381 TFE 20 Polyphenylene Sulfide (PPS) Carbon Fiber - PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.49 g/cc
1.49 g/cc
ASTM D 792
Additive Loading 10 %
10 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0020 cm/cm

@Thickness 3.20 mm
0.00050 - 0.0020 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 124 MPa
18000 psi
ASTM D 638
Elongation at Break 1.0 - 1.5 %
1.0 - 1.5 %
ASTM D 638
Tensile Modulus 12.8 GPa
1850 ksi
ASTM D 638
Flexural Strength 176 MPa
25500 psi
ASTM D 790
Flexural Modulus 11.0 GPa
1600 ksi
ASTM D 790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.20 mm
0.800 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 2.40 J/cm

@Thickness 3.20 mm
4.50 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+6 ohm-cm
<= 1.00e+6 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 307 - 329 °C
585 - 625 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 21600 sec
300 °F

@Time 6.00 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi