RTP Company RTP 1383 HEC Polyphenylene Sulfide (PPS), Nickel-Coated Carbon Fiber - Electrically Conductive - EMI/RFI/ESD Protection

Category Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS), Conductive
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1383 HEC Polyphenylene Sulfide (PPS), Nickel-Coated Carbon Fiber - Electrically Conductive - EMI/RFI/ESD Protection.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.50 g/cc
1.50 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Linear Mold Shrinkage 0.00050 - 0.0015 cm/cm

@Thickness 3.17 mm
0.00050 - 0.0015 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 128 MPa
18500 psi
ASTM D 638
Elongation at Break 1.0 - 2.0 %
1.0 - 2.0 %
ASTM D 638
Tensile Modulus 12.1 GPa
1750 ksi
ASTM D 638
Flexural Strength 190 MPa
27500 psi
ASTM D 790
Flexural Modulus 12.4 GPa
1800 ksi
ASTM D 790
Izod Impact, Notched 0.427 J/cm

@Thickness 3.17 mm
0.800 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 2.14 J/cm

@Thickness 3.17 mm
4.00 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Electrical Properties Metric English Comments
Volume Resistivity <= 1.0 ohm-cm
<= 1.0 ohm-cm
ASTM D 257
Surface Resistance <= 1000 ohm
<= 1000 ohm
ESD STM11.11
Surface Resistivity per Square <= 10000 ohm
<= 10000 ohm
ASTM D 257
Static Decay <= 2.0 sec
<= 2.0 sec
MIL-PRF-81705D, 5kV to 50 V, 12% RH; FTMS101C; 4046.1
Processing Properties Metric English Comments
Melt Temperature 307 - 329 °C
585 - 625 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi