RTP Company RTP 1400 AG-220 Polyethersulfone (PES), Glass Fiber - UL94 V-0

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 20%Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1400 AG-220 Polyethersulfone (PES), Glass Fiber - UL94 V-0.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.51 g/cc
1.51 g/cc
ASTM D 792
Filler Content 20 %
20 %
Primary Additive
Water Absorption 0.40 %
0.40 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0030 - 0.0050 cm/cm

@Thickness 3.17 mm
0.0030 - 0.0050 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D 785
Tensile Strength at Break 103 MPa
15000 psi
ASTM D 638
Elongation at Break 3.0 - 4.0 %
3.0 - 4.0 %
ASTM D 638
Tensile Modulus 5.52 GPa
800 ksi
ASTM D 638
Flexural Strength 169 MPa
24500 psi
ASTM D 790
Flexural Modulus 5.52 GPa
800 ksi
ASTM D 790
Izod Impact, Notched 0.481 J/cm

@Thickness 3.17 mm
0.900 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 6.67 J/cm

@Thickness 3.17 mm
12.5 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 209 °C
408 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 0.7937 mm
V-0

@Thickness 0.03125 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+16 ohm-cm
>= 1.00e+16 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi