RTP Company RTP 1400 AG-330 Polyethersulfone (PES), Glass Fiber

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 30%Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1400 AG-330 Polyethersulfone (PES), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.58 g/cc
1.58 g/cc
ASTM D 792
Additive Loading 30.0 %
30.0 %
Primary Additive
Linear Mold Shrinkage 0.00200 cm/cm

@Thickness 3.20 mm
0.00200 in/in

@Thickness 0.126 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
ASTM D 638
Elongation at Break 2.50 %
2.50 %
ASTM D 638
Tensile Modulus 8.96 GPa
1300 ksi
ASTM D 638
Flexural Strength 193 MPa
28000 psi
ASTM D 790
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D 790
Izod Impact, Notched 0.801 J/cm

@Thickness 3.20 mm
1.50 ft-lb/in

@Thickness 0.126 in
ASTM D 256
Izod Impact, Unnotched 6.41 J/cm

@Thickness 3.20 mm
12.0 ft-lb/in

@Thickness 0.126 in
ASTM D 4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 28.8 µm/m-°C
16.0 µin/in-°F
E 831
CTE, linear, Transverse to Flow 93.6 µm/m-°C
52.0 µin/in-°F
E 831
Deflection Temperature at 0.46 MPa (66 psi) 216 °C
420 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C

@Time 21600 sec
300 °F

@Time 6.00 hour
Moisture Content 0.0400 %
0.0400 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi