RTP Company RTP 1401 N Polyethersulfone (PES), Glass Fiber - High Viscosity

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 10%Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1401 N Polyethersulfone (PES), Glass Fiber - High Viscosity.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.44 g/cc
1.44 g/cc
ASTM D 792
Filler Content 10 %
10 %
Primary Additive
Water Absorption 0.40 %
0.40 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0060 cm/cm

@Thickness 3.17 mm
0.0060 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D 785
Tensile Strength at Break 103 MPa
15000 psi
ASTM D 638
Elongation at Break 4.0 %
4.0 %
ASTM D 638
Tensile Modulus 4.48 GPa
650 ksi
ASTM D 638
Flexural Strength 159 MPa
23000 psi
ASTM D 790
Flexural Modulus 4.14 GPa
600 ksi
ASTM D 790
Compressive Strength 110 MPa
16000 psi
ASTM D 695
Izod Impact, Notched 0.747 J/cm

@Thickness 3.17 mm
1.40 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 5.87 J/cm

@Thickness 3.17 mm
11.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 43.2 µm/m-°C
24.0 µin/in-°F
E 831
Thermal Conductivity 0.288 W/m-K
2.00 BTU-in/hr-ft²-°F
Through-plane; E 1530
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 204 °C
400 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
ASTM D 257
Dielectric Constant 3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 15.0 kV/mm
380 kV/in
Short Term; in oil; ASTM D 149
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Arc Resistance 70 sec
70 sec
ASTM D 495
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi