RTP Company RTP 1407 Polyethersulfone (PES), Glass Fiber

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone (PES), 40%Glass Fiber Filled
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1407 Polyethersulfone (PES), Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D 792
Filler Content 40 %
40 %
Primary Additive
Water Absorption 0.30 %
0.30 %
24 hrs @ 23°C; ASTM D 570
Linear Mold Shrinkage 0.0010 cm/cm

@Thickness 3.17 mm
0.0010 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ASTM D 785
Tensile Strength at Break 159 MPa
23000 psi
ASTM D 638
Elongation at Break 2.1 %
2.1 %
ASTM D 638
Tensile Modulus 12.4 GPa
1800 ksi
ASTM D 638
Flexural Strength 224 MPa
32500 psi
ASTM D 790
Flexural Modulus 11.7 GPa
1700 ksi
ASTM D 790
Compressive Strength 152 MPa
22000 psi
ASTM D 695
Izod Impact, Notched 0.961 J/cm

@Thickness 3.17 mm
1.80 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 6.67 J/cm

@Thickness 3.17 mm
12.5 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.2 µm/m-°C
14.0 µin/in-°F
E 831
Thermal Conductivity 0.360 W/m-K
2.50 BTU-in/hr-ft²-°F
Through-plane; E 1530
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 216 °C
420 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+12 ohm-cm
>= 1.00e+12 ohm-cm
ASTM D 257
Dielectric Constant 4.3

@Frequency 1.00e+6 Hz
4.3

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Dielectric Strength 14.6 kV/mm
370 kV/in
Short Term; in oil; ASTM D 149
Dissipation Factor 0.0070

@Frequency 1.00e+6 Hz
0.0070

@Frequency 1.00e+6 Hz
Dry; ASTM D 150
Arc Resistance 80 sec
80 sec
ASTM D 495
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi