RTP Company RTP 1481 TFE 10 Polyethersulfone (PES), Carbon Fiber - PTFE Lubricated

Category Polymer , Thermoplastic , Polyethersulfone (PES) , Polyethersulfone, Carbon Fiber Reinforced
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 1481 TFE 10 Polyethersulfone (PES), Carbon Fiber - PTFE Lubricated.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.45 g/cc
1.45 g/cc
ASTM D 792
Filler Content 10 %
10 %
Primary Additive
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 145 MPa
21000 psi
ASTM D 638
Elongation at Break 1.5 - 3.0 %
1.5 - 3.0 %
ASTM D 638
Tensile Modulus 9.65 GPa
1400 ksi
ASTM D 638
Flexural Strength 207 MPa
30000 psi
ASTM D 790
Flexural Modulus 8.96 GPa
1300 ksi
ASTM D 790
Izod Impact, Notched 0.587 J/cm

@Thickness 3.17 mm
1.10 ft-lb/in

@Thickness 0.125 in
D 256
Izod Impact, Unnotched 5.34 J/cm

@Thickness 3.17 mm
10.0 ft-lb/in

@Thickness 0.125 in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 218 °C
425 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity 1000 - 1.00e+6 ohm-cm
1000 - 1.00e+6 ohm-cm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 343 - 377 °C
650 - 710 °F
Mold Temperature 135 - 177 °C
275 - 350 °F
Drying Temperature 149 °C
300 °F
Dry Time 6 hour
6 hour
Moisture Content 0.040 %
0.040 %
Dew Point -31.7 °C
-25.0 °F
Injection Pressure 68.9 - 103 MPa
10000 - 15000 psi