RTP Company RTP 200 TC-C-20 FR Nylon 6/6 (PA), Thermally Conductive - Electrically Conductive - Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 200 TC-C-20 FR Nylon 6/6 (PA), Thermally Conductive - Electrically Conductive - Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.68 g/cc
1.68 g/cc
ASTM D 792
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 3.17 mm
0.0010 - 0.0030 in/in

@Thickness 0.125 in
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 138 MPa
20000 psi
ASTM D 638
Elongation at Break 1.0 %
1.0 %
ASTM D 638
Tensile Modulus 22.8 GPa
3300 ksi
ASTM D 638
Flexural Strength 207 MPa
30000 psi
ASTM D 790
Flexural Modulus 20.7 GPa
3000 ksi
ASTM D 790
Izod Impact, Notched 0.534 J/cm

@Thickness 3.17 mm
1.00 ft-lb/in

@Thickness 0.125 in
ASTM D 256
Izod Impact, Unnotched 3.74 J/cm

@Thickness 3.17 mm
7.00 ft-lb/in

@Thickness 0.125 in
ASTM D 4812
Thermal Properties Metric English Comments
Thermal Conductivity 1.30 W/m-K
9.00 BTU-in/hr-ft²-°F
Through-plane; ASTM E 1530
2.74 W/m-K
19.0 BTU-in/hr-ft²-°F
In-plane; ASTM E 1461-92
Deflection Temperature at 1.8 MPa (264 psi) 232 °C
450 °F
ASTM D 648
Flammability, UL94 V-0

@Thickness 1.59 mm
V-0

@Thickness 0.0625 in
Electrical Properties Metric English Comments
Volume Resistivity <= 100 ohm-cm
<= 100 ohm-cm
ASTM D 257
Surface Resistivity per Square <= 10000 ohm
<= 10000 ohm
ASTM D 257
Processing Properties Metric English Comments
Melt Temperature 277 - 299 °C
530 - 570 °F
Mold Temperature 65.6 - 107 °C
150 - 225 °F
Drying Temperature 79.4 °C

@Time 14400 sec
175 °F

@Time 4.00 hour
Moisture Content 0.20 %
0.20 %
Dew Point -17.8 °C
0.000 °F
Injection Pressure 68.9 - 124 MPa
10000 - 18000 psi