RTP Company RTP 2800 B-55A UV Thermoplastic Polyolefin Elastomer (TEO), UV Stabilized  (discontinued **)

Category Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 2800 B-55A UV Thermoplastic Polyolefin Elastomer (TEO), UV Stabilized  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
Physical Properties Metric English Comments
Specific Gravity 0.970 g/cc
0.970 g/cc
ASTM D 792
Linear Mold Shrinkage 0.019 - 0.024 cm/cm

@Thickness 3.17 mm
0.019 - 0.024 in/in

@Thickness 0.125 in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 57
57
10 s delay; ASTM D 2240
Tensile Strength at Break 4.48 MPa
650 psi
Break; 20 in/min (500 mm/min); ASTM D 412
Tensile Strength, Yield 0.965 MPa

@Strain 50.0 %
140 psi

@Strain 50.0 %
ASTM D 412
1.59 MPa

@Strain 100 %
230 psi

@Strain 100 %
ASTM D 412
2.83 MPa

@Strain 300 %
410 psi

@Strain 300 %
ASTM D 412
Elongation at Break 600 %
600 %
20 in/min (500 mm/min); ASTM D 412
Tear Strength 21.0 kN/m
120 pli
Die C; ASTM D 624
Compression Set 22 %

@Temperature 23.0 °C,
Time 79200 sec
22 %

@Temperature 73.4 °F,
Time 22.0 hour
Method B; Type 2; ASTM D 395
38 %

@Temperature 70.0 °C,
Time 79200 sec
38 %

@Temperature 158 °F,
Time 22.0 hour
Method B; Type 2; ASTM D 395
Thermal Properties Metric English Comments
Flammability, UL94 HB

@Thickness 1.59 mm
HB

@Thickness 0.0625 in
Processing Properties Metric English Comments
Melt Temperature 193 - 210 °C
380 - 410 °F
Mold Temperature 10.0 - 79.4 °C
50.0 - 175 °F
Drying Temperature 79.4 °C
175 °F
Dry Time 3 - 4 hour
3 - 4 hour
Moisture Content <= 0.080 %
<= 0.080 %
Injection Pressure 34.5 - 68.9 MPa
5000 - 10000 psi