- RTP Company RTP 285D TFE 10 Nylon 6/12 (PA 6/12) Carbon Fiber 30% - PTFE 10% (discontinued
RTP Company RTP 285D TFE 10 Nylon 6/12 (PA 6/12) Carbon Fiber 30% - PTFE 10% (discontinued
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612, Carbon Fiber Filler |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 285D TFE 10 Nylon 6/12 (PA 6/12) Carbon Fiber 30% - PTFE 10%
(discontinued.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Carbon Fiber 30% - PTFE 10%Comments:Carbon FiberPTFE LubricatedUnless otherwise specified, all data listed is for natural or black colored materials. Pigments can affect properties.Information provided by RTP Company.Data for this product has not been recently verified, please contact RTP Company for more information before specifying this grade.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.29 g/cc | 1.29 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.14 % | 0.14 % | 24 hours at 23°C; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.17 mm |
0.0010 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0020 cm/cm @Thickness 6.35 mm |
0.0020 in/in @Thickness 0.250 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 207 MPa | 30000 psi | ASTM D638 |
| Elongation at Break | 2.0 - 3.0 % | 2.0 - 3.0 % | ASTM D638 |
| Modulus of Elasticity | 25.5 GPa | 3700 ksi | ASTM D638 |
| Flexural Yield Strength | 331 MPa | 48000 psi | ASTM D790 |
| Flexural Modulus | 20.7 GPa | 3000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.17 J/cm @Thickness 3.17 mm |
2.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Izod Impact, Unnotched | 10.7 J/cm @Thickness 3.17 mm |
20.0 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 216 °C | 420 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
Per testing by RTP Company; ASTM D635 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 100 ohm-cm | 100 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 252 - 279 °C | 485 - 535 °F | |
| Mold Temperature | 60.0 - 93.3 °C | 140 - 200 °F | |
| Injection Pressure | 68.9 - 124 MPa | 10000 - 18000 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Natural/Black |
Users viewing this material also viewed the following:
- PTS PBT-1100A PBT Resin
- NuSil MED-346 Simethicone
- LyondellBasell Petrothene® LB560401 High Density Polyethylene
- IRPC Polimaxx Pentfoam 155E Expandable Polystyrene
- Heatbath/Park Thermo-Quench Oil
- LG Chemical LUPOL GP-3152F General Purpose Polypropylene, 15% Mineral Fillers, High Impact, Flame Retardant
- RTP Company RTP 200 A TFE 13 SI 2 Nylon 6 (PA), PTFE Lubricated - Silicone Lubricated
- DSM Akulon® K222-KGV4 Nylon 6-20% Glass Reinforced (European and Asian Grade) (Cond)
- Carmel Olefins CAPILENE® SW 75 AV Polypropylene Impact Copolymer
- HP Alloys HPA COBALT Alloy 6B, Wear Resistant, (Co-Cr-W) (UNS R30016)
Copyright © lookpolymers.com All Rights Reserved