- Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant
- RTP Company RTP 3999X56542A Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant (discontinued **)
RTP Company RTP 3999X56542A Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant (discontinued **)
| Category | Polymer , Thermoplastic , Polyketone , Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | RTP Company RTP 3999X56542A Polyetherketoneetherketoneketone (PEKEKK), Wear Resistant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data is for injection molded specimens and was provided by the manufacturer, RTP Company.This product has been discontinued, please contact RTP Company regarding alternate grades.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | 24 hrs @ 23°C; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
ASTM D955 |
| 0.0020 cm/cm @Thickness 6.40 mm |
0.0020 in/in @Thickness 0.252 in |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Tensile Modulus | 12.4 GPa | 1800 ksi | ASTM D638 |
| Flexural Yield Strength | 217 MPa | 31500 psi | ASTM D790 |
| Flexural Modulus | 9.00 GPa | 1310 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.20 mm |
1.69 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Izod Impact, Unnotched | 5.30 J/cm @Thickness 3.20 mm |
9.93 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | at 50 fpm, 2000 PV against C1018 Steel HRC 15-25, 14-17 microsmoothness; ASTM D 3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 316 °C | 601 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Values per RTP Company Testing.; UL94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 10.0 ohm-cm | 10.0 ohm-cm | ASTM D257 |