RTP Company RTP 6003-75A Z Specialty Thermoplastic Elastomer, FDA Compliant Ingredients

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer RTP Company
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF RTP Company RTP 6003-75A Z Specialty Thermoplastic Elastomer, FDA Compliant Ingredients.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Physical Properties Metric English Comments
Specific Gravity 1.02 g/cc
1.02 g/cc
ASTM D 792
Linear Mold Shrinkage 0.013 cm/cm

@Thickness 3.17 mm
 0.013 in/in

@Thickness 0.125 in
 ASTM D955
Mechanical Properties Metric English Comments
Hardness, Shore A 75
75
10 s delay; ASTM D 2240
Tensile Strength at Break 6.21 MPa

@Thickness 3.17 mm
 900 psi

@Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
Tensile Strength, Yield 3.10 MPa

@Strain 50.0 %,
Thickness 3.17 mm
 450 psi

@Strain 50.0 %,
Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
3.45 MPa

@Strain 100 %,
Thickness 3.17 mm
 500 psi

@Strain 100 %,
Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
4.83 MPa

@Strain 100 %,
Thickness 3.17 mm
 700 psi

@Strain 100 %,
Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
Elongation at Break 850 %

@Thickness 3.17 mm
 850 %

@Thickness 0.125 in
 Die C; 20 in/min (500 mm/min); ASTM D412
Tear Strength 43.8 kN/m
250 pli
Die C; ASTM D 624
Compression Set 23 %

@Temperature 23.0 °C,
Time 79200 sec
 23 %

@Temperature 73.4 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
65 %

@Temperature 70.0 °C,
Time 79200 sec
 65 %

@Temperature 158 °F,
Time 22.0 hour
 Method B; Type 2; ASTM D 395
Processing Properties Metric English Comments
Melt Temperature 193 - 238 °C
380 - 460 °F
Mold Temperature 21.1 - 48.9 °C
70.0 - 120 °F
Drying Temperature 76.7 °C
170 °F
Dry Time 2 - 4 hour
2 - 4 hour
Moisture Content 0.040 %
0.040 %
Injection Pressure 34.5 - 103 MPa
5000 - 15000 psi