Radici Radilon® A ERV3012 (dry) Nylon 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer Radici Group Plastics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Radici Radilon® A ERV3012 (dry) Nylon 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Radilon® A is a range of polyamide 66 (PA66) products obtained through the polymerization of hexamethylendiamine and adipic acid, and used for injection, extrusion and blow-molding.Information provided by Radici group.
Physical Properties Metric English Comments
Specific Gravity 1.21 g/cc
1.21 g/cc
Water Absorption 6.7 %
6.7 %
Moisture Absorption at Equilibrium 1.8 %
1.8 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
Elongation at Break 4.2 %
4.2 %
Tensile Modulus 5.30 GPa
769 ksi
Charpy Impact Unnotched 6.80 J/cm²

@Temperature 23.0 °C
32.4 ft-lb/in²

@Temperature 73.4 °F
7.00 J/cm²

@Temperature -30.0 °C
33.3 ft-lb/in²

@Temperature -22.0 °F
Charpy Impact, Notched 0.950 J/cm²

@Temperature -30.0 °C
4.52 ft-lb/in²

@Temperature -22.0 °F
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 260 °C
500 °F
Deflection Temperature at 0.46 MPa (66 psi) 240 °C
464 °F
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
Vicat Softening Point 225 °C

@Load 5.10 kg
437 °F

@Load 11.2 lb
50°C/h
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+11 ohm-cm
>= 1.00e+11 ohm-cm